How to Use DMC Catalyst to Produce Polyether Polyols？
The DMC catalyst is double metal cyanide catalyst. Compared with similar polyols made using basic(e.g., KOH)catalysts, polyether polyols made from the catalyst have low unsaturations, narrow molecular weight distributions, have high molecular weight, and are useful in making a variety of polyurethane products. DMC catalyst is highly active in epoxide polymerization reactions used to prepare polyether polyols.
We can yield the DMC more than 20000 kg within one year, and thus afford to produce 50～70 ten thousand tons of polyols. This catalyst is white or light yellow powder, is suitable for preparation of polyols with 1~6 functions. Compared with basic catalysts, this catalyst can be used with less amount (30ppm), and reaction time of polymerization is reduced largely, and the polyols products are not necessary to be refined. The DMC is suitable for using in common epoxide polymerization reactors, but it can be better if reactors have both of stirring and cycling systems.
When using the DMC production period is short, thus the costs for production are reduced while the property of products are advanced.
Conditions wanted for initiators
1. polyethers with 1～3 0r more hydroxyl groups 2. molecular weight:for at least 2 hydroxyl groups---350~1000; for monols---with boiling point more than l00℃ 3. ∑Mn+ (mainly for K、Naions)≤5ppm 4. water content≤0.1% 5. acid value≤0.15mgKOH/g
Applying procedure
1. Weigh certain amount of initiator and the catalyst. The catalyst's amount is generally 30ppm relative to the product (it mainly refers to N220 with 2 hydroxyl groups and N330 with 3 hydroxyl groups). The amount of the catalyst can reduce if the molecular weight of products are relatively high, e.g. for N240, the amount can be 20～25ppm. 2. The mixture is stirred and is stripped under a vacuum with pressure less than l0 mm (Hg), and is heated to 130~145℃ to remove traces of water from the starter. Generally it needs more than 40min after the temperature rises to 130~145℃. 3. Propylene oxide (PO) or mixture of ethylene oxide (EO) and PO is fed to the reactor, under a pressure of 0.1—0.25Mpa. Additional PO or PO and EO is not added until an accelerated pressure drop occurs in the reactor (temperature can reach above 180℃,but this can not harm the activity of DMC or the properties of products). PO or PO and EO is added while maintaining a reactor pressure generally less than 0.1Mpa,temperature 140±10℃. 4. After PO or PO and EO addition is complete, the mixture is held at 140±5℃ until a constant pressure is observed. Residual unreacted monomer (generally only traces) is then stripped.
May 17, 2022The most beautiful encounter is reunion, and every reunion will definitely leave a beautiful mark in our lives.--NCMC The much-anticipated China International Cleanser Ingredients Machinery & Pack...view
March 26, 2025China Amphoteric Surfactants have both anionic and cationic surfactant properties and are generally used as auxiliary components in detergents rather than as the main detergent. Their primary function...view
November 2, 2023Textile innovation has come a long way, with advances in materials, production techniques, and sustainability. In the quest for more functional and versatile textiles, expandable microspheres have eme...view
September 23, 20212-chloropropionic acid is a pale liquid with a slight odor and is the simplest chiral chlorocarboxylic acid. The formula of 2-Chloropropionic acid is CH3CHClCO2H. It is produced by chlorination of pro...view
January 26, 2024Today, we are going to explore the remarkable role of 1,2-EPOXYBUTANE in advancing pharmaceutical research and development. From its synthesis to potential applications in drug discovery, this compoun...view
January 3, 2024The medical field is continually advancing, thanks to innovations in materials and technology. One such innovation is the use of expandable microspheres, and the producers of these microspheres have p...view
Cinnamic Acid
Product InformationProduct Name: Cinnamic acid Chemical Formula: C9H8O2CAS No.: 621-82-9Dangerous Grade: NoneTechnical Data:ItemSpecificationAppearancewhite to slightly yellow powderAssay 99%min.M...
Modified PU Structure Adhesive 2
SystemWINNATE/WINCUREAdvantage·Anti-moisture, non-foaming·No VOC (non-plasticizer, non-thinner)·Hydrophobic resin system, non-need to pre-dry of substrate·Self-reinforcement and flame retardant·C...